Behaviour of short and long cracks in air and in liquid metal in T91 steel

Abstract : The low cycle fatigue behaviour of a 9Cr1MoNbV martensitic steel has been investigated at 350°C in air and in lead-bismuth eutectic (LBE).Total strain controlled tests were performed from Δεt=0.40% to 1.2%. The material exhibited a pronounced cyclic softening in both environments. LBE reduced the fatigue resistance. LBE accelerated the formation of the long crack by promoting the growth ofthe first short cracks. A clear change in propagation mode was observed. In air, ductile fatigue striations were observed while in LBE a brittle fracture decorated by voluminous and largely spaced striations were visible. From EBSD analysis,it was concluded that in LBE, the long crack advanced quickly by repeated and discontinuous cleavage.
Type de document :
Communication dans un congrès
Liste complète des métadonnées

Littérature citée [9 références]  Voir  Masquer  Télécharger
Contributeur : Lilloa Université de Lille <>
Soumis le : mercredi 4 septembre 2019 - 08:29:46
Dernière modification le : vendredi 28 février 2020 - 15:00:22


Fichiers éditeurs autorisés sur une archive ouverte


Distributed under a Creative Commons Paternité 4.0 International License



Jean Bernard Vogt, Carla Carlé, Jeremy Bouquerel, Ingrid Proriol Serre. Behaviour of short and long cracks in air and in liquid metal in T91 steel. FATIGUE 2018, May 2018, Poitiers, France. ⟨10.1051/matecconf/201816503016⟩. ⟨hal-02277927v1⟩



Consultations de la notice


Téléchargements de fichiers