On the Nanoscale Mapping of the Mechanical and Piezoelectric Properties of Poly (L-Lactic Acid) Electrospun Nanofibers - Université de Lille Accéder directement au contenu
Article Dans Une Revue Applied Sciences Année : 2020

On the Nanoscale Mapping of the Mechanical and Piezoelectric Properties of Poly (L-Lactic Acid) Electrospun Nanofibers

Résumé

The effect of the post-annealing process on different properties of poly (L-lactic acid) (PLLA) nanofibers has been investigated in view of their use in energy-harvesting devices. Polymeric PLLA nanofibers were prepared by using electrospinning and then were thermally treated above their glass transition. A detailed comparison between as-spun (amorphous) and annealed (semi-crystalline) samples was performed in terms of the crystallinity, morphology and mechanical as well as piezoelectric properties using a multi-technique approach combining DSC, XRD, FTIR, and AFM measurements. A significant increase in the crystallinity of PLLA nanofibers has been observed after the post-annealing process, together with a major improvement of the mechanical and piezoelectric properties.
Fichier principal
Vignette du fichier
34 - 2020 - On the Nanoscale Mapping of the Mechanical and Piezoelectric Properties of Poly (L‐Lactic Acid) Electrospun Nanofibers.pdf (1.66 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte
Loading...

Dates et versions

hal-02444046 , version 1 (17-01-2020)

Licence

Paternité

Identifiants

Citer

Cuong Nguyen Thai, Sophie Barrau, Malo Dufay, Nicolas Tabary, Antonio Da Costa, et al.. On the Nanoscale Mapping of the Mechanical and Piezoelectric Properties of Poly (L-Lactic Acid) Electrospun Nanofibers. Applied Sciences, 2020, Applied Sciences, 10 (2), pp.652. ⟨10.3390/app10020652⟩. ⟨hal-02444046⟩
62 Consultations
92 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More