Amorphous silicate nanoparticles with controlled Fe-Mg pyroxene compositions

Abstract : The production of amorphous pyroxene nanoparticles (~ 20 nm) with controlled Fe-Mg content is described. Homogenous particle compositions closely matching required target stoichiometries are obtained by drying a precursor gel under high vacuum conditions. The silicate nature of the particles is characterised using TEM, synchrotron radiation and FTIR. No oxide phase separation occurs, even at high Fe concentration. Structural domains exist within the nanoparticles that are typically ten times smaller than the physical particle size consistent with either a core-shell, or, random network with multiple embedded domains, particle structure. Thermal annealing below the crystallisation temperature allows the ordered domain size to be further reduced by a factor of ~ 2.
Liste complète des métadonnées

https://hal.univ-lille.fr/hal-03138519
Contributeur : Lilloa Université de Lille <>
Soumis le : jeudi 11 février 2021 - 16:53:42
Dernière modification le : vendredi 12 février 2021 - 03:34:23

Fichier

A Evans - Amorphous silicate n...
Fichiers produits par l'(les) auteur(s)

Identifiants

Collections

Citation

Stephen P. Thompson, Karine Demyk, Sarah J. Day, Aneurin Evans, Hugues Leroux, et al.. Amorphous silicate nanoparticles with controlled Fe-Mg pyroxene compositions. Journal of Non-Crystalline Solids, Elsevier, 2016, Journal of Non-Crystalline Solids, 447, pp.255-261. ⟨10.1016/j.jnoncrysol.2016.06.017⟩. ⟨hal-03138519⟩

Partager

Métriques

Consultations de la notice

75

Téléchargements de fichiers

28