Formulation of metal-organic fr amework inks for the 3D printing of robust microporous solids
Résumé
Metal-organic frameworks (MOFs) are a fast-growing class of highly porous materials owing to their exceptional structural diversity. A consequent effort has been deployed during the past few years for rationalizing the preparation of the most promising MOF structures, in view of their applications at larger scale. Still, their shaping represents a major bottleneck due to the difficulty to conciliate high porosity and adequate mechanical resistance to withstand overtime damaging stresses.
3D printing is a promising technology as it allows the fast prototyping of materials at the macroscale.1 Herein, a 3D printer was modified to prepare a variety of MOF-based solids with controlled morphology from shear-thinning inks containing a cellulose-derived binder. Four benchmark MOFs were tested: HKUST-1, CPL-1, ZIF-8 and UiO-66-NH2. All solids are mechanically stable up to 0.6 MPa of uniaxial compression and highly porous, with BET specific surface areas lowered by 0 to -25%. Furthermore, these solids were applied to high pressure sorption (CH4, C2H4 and C2H6) and presented performances in line with the literature.
Domaines
CatalyseFormat | typeAnnex_author |
---|