Development and Multiscale Characterization of 3D Warp Interlock Flax Fabrics with Different Woven Architectures for Composite Applications - Université de Lille Accéder directement au contenu
Article Dans Une Revue Fibers Année : 2020

Development and Multiscale Characterization of 3D Warp Interlock Flax Fabrics with Different Woven Architectures for Composite Applications

Résumé

Multiscale characterization of the textile preform made of natural fibers is an indispensable way to understand and assess the mechanical properties and behavior of composite. In this study, a multiscale experimental characterization is performed on three-dimensional (3D) warp interlock woven fabrics made of flax fiber on the fiber (micro), roving (meso), and fabric (macro) scales. The mechanical tensile properties of the flax fiber were determined by using the impregnated fiber bundle test. The effect of the twist was considered in the back-calculation of the fiber stiffness to reveal the calculation limits of the rule of mixture. Tensile tests on dry rovings were carried out while considering different twist levels to determine the optimal amount of twist required to weave the flax roving into a 3D warp interlock. Finally, at fabric-scale, six different 3D warp interlock architectures were woven to understand the role of the architecture of binding rovings on the mechanical properties of the dry 3D fabric. The results reveal the importance of considering the properties of the fiber and roving at these scales to determine the more adequate raw material for weaving. Further, the characterization of the 3D woven structures shows the preponderant role of the binding roving on their structural and mechanical properties.
Fichier principal
Vignette du fichier
fibers-08-00015-v2.pdf (7.46 Mo) Télécharger le fichier
Origine Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-04504116 , version 1 (14-03-2024)

Licence

Identifiants

Citer

Henri Lansiaux, Damien Soulat, Francois Boussu, Ahmad Rashed Labanieh. Development and Multiscale Characterization of 3D Warp Interlock Flax Fabrics with Different Woven Architectures for Composite Applications. Fibers, 2020, Fibers, 8 (2), ⟨10.3390/fib8020015⟩. ⟨hal-04504116⟩

Collections

UNIV-LILLE
5 Consultations
4 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More